Chemical composition of the weld formation at high concentrated energy source welding in vacuum
Ekaterina S. Salomatova, Dmitrii N. Trushnikov, Tatiana V. Olshanskaya, Vladimir Ya. Belenkiy
Results of numerical modeling of formation of a final chemical composition at electron beam welding with oscillations and dynamic splitting of an electronic beam on three thermal sources are presented in this article. Verification of settlement data with experimental data is carried out. For a pilot study of the chemical composition of the welded seams X-ray fluorescent analysis on the crosssections is executed on various modes has been carried out. When processing experimental data the dependences of the concentration of the easily evaporated elements on the welding process parameters have been constructed.
Тази статия представя резултатите от цифрова симулация на формирането на крайния химическия състав при електроннолъчево заваряване с колебания и динамично разделяне на електронния лъч на три топлинни източника. Направена е проверка на изчислените данни с експериментални данни. За начално изследване на химическия състав на заваръчните шлифове е проведен рентгено-флуорисцентен анализ при различни параметри. При обработката на експерименталните данни е намерена зависимостта на концентрацията на леснолетливите елементи от параметрите концентрацията е на летливи елементи от параметрите на заваръчния процес.
Cite this article as:
Salomatova E. S., Trushnikov D. N., Olshanskaya T. V., Belenkiy V. Ya. Chemical composition of the weld formation at high concentrated energy source welding in vacuum. Journal – Electrotechnica & Electronica (Е+Е), Vol. 51 (5-6), 2016, pp. 103-107, ISSN: 0861-4717 (Print), 2603-5421 (Online)