Flash electron beam welding of stainless steels 1.4510 and 1.4511
Jiří Matlák, Ivan Šipula, Václav Štraus, Ivo Dlouhý
The electron beam technology allows a rapid scanning along a defined trajectory. When a properly controlled input of energy is applied, it could be used for the manufacturing of a whole weld joint at once. This technology, called flash welding, represents an alternative to common continuous welding.
The aim of the paper is to describe the development of the procedure for a given weld joint geometry and the effect of the welding parameters on selected properties of the weld joint. The circle welds were manufactured on the samples of materials 1.4510 and 1.4511 by using the electron beam facility K26 from ProBeam. The properties of the welds were examined by the light microscopy and the microhardness testing. Final results were discussed based on analysis of EB elding conditions and weld joint parameters.
Електроннолъчевата технология позволява бързо сканиране по определена траектория. Когато се приложи един правилно подбран енергиен вход, може да се произведе целия шев едновременно. Тази технология, наречена мигновено заваряване, представя една алтернатива на съвременното непрекъснато заваряване.
Цел на работата е да опише развитието на процедурите за дадена геометрия на заваръчното съединение и ефекта на заваръчните параметри върху избраните свойства на заваръчния шев. Кръгови шевове бяха получени на образци от стомани 1.4510 и 1.4511, използвайки устройството К26 на ProBeam. Свойствата на шевовете бяха изпитани със светлинен микроскоп и микротвърдностни изпитания. Крайният резултат се дискутират на основата на ЕЛ заваръчните условия и параметрите на електроннолъчевия шев.