Derivation and analysis of ceramic materials based on BaTiO3 by using standard ceramic technology
Valentin Kolev, Anka Zeglova, Ivailo Lazarov
Ceramic materials based on BaTiO3 have been derived by using a standard ceramic technology. Various quantities of H3BO3 and Bi3O3 have been added in order to lower the temperature of synthesis. For the researched material, an X-ray diffraction analysis was carried out. The dependencies of the density, the relative permittivity and the contraction on the temperature of sintering, have been obtained. The addition of H3BO3 leads to higher density values, but the dielectric permeability is not high. The addition of Bi3O3 assures a liquid stage during the synthesis and supports the solid-phase reactions. The highest relative dielectric permeability values were obtained for the ceramic material by simultaneous addition of H3BO3 and Bi3O3
Керамични материали на основата на BaTiO3 са получени чрез използване на стандартна керамична технология. За намаляване температурата на синтез са използвани различни количества H3BO3 и Bi3O3. На изследваните материали е проведен рентгеноструктурен анализ. Получени са зависимостите на плътността, относителната диелектрична проницаемост и свиването в зависимост от температурата на синтез. Прибавянето на H3BO3 води до добри стойности на плътността, но диелектричната проницаемост не е висока. Добавката Bi3O3 обезпечава течна фаза при синтеза и улеснява твърдофазните реакции. Най-високи стойности за относителната диелектрична проницаемост са получени при керамични материали с едновременно добавени H3BO3 и Bi3O3.
Cite this article as:
Kolev V., Zeglova A., Lazarov I. Derivation and analysis of ceramic materials based on BaTiO3 by using standard ceramic technology. Journal – Electrotechnica & Electronica (Е+Е), Vol. 50 (5-6), 2015, pp. 12-17, ISSN: 0861-4717 (Print), 2603-5421 (Online)