Electron Beam Sintering of Ceramics
Aleksandr S. Klimov, Aleksey А. Zenin, Efim М. Oks, Oleg L. Khasanov, Edgar S. Dvilis, Aleksei О. Khasanov
Results on application of electron beam in fore-vacuum for ceramic sintering are presented. Three types of ceramic were investigated: aluminum oxide Al2O3, zirconium oxide YSZ and silicon carbide SiC. Different behavior for all these materials is observed. Al2O3 tends to grain size growth during sintering. On the contrary, grain size of YSZ decreases with sintering duration. Both these materials become more dense after sintering. At the same time the structure of SiC becomes more porous. Properties differ significantly along the sample. Electron beam sintering is carried out at lower temperatures than usual sintering in furnace.
Представени са резултати от синтероването на керамика чрез приложение на електронен лъч при форвакуум. Изследвани са три типа керамика: алуминиев оксид Al2O3, циркониев оксид YSZ и силициев карбид SiC. Наблюдавано е различно поведение на всички тези материали. Al2O3 клони към нарастване на размера на зърната по време на синтероването. Обратно, размера на зърното на YSZ намалява по време на синтероването. И двата материала стават по-плътни след синтеруване. В същото време структурата на SiC става по-пореста. Свойствата се различават значимо по протежение на образеца. Електроннолъчевото синтероване се провежда при по-ниски температури от типичното синтероване в пещ.
Cite this article as:
Klimov А. S., Zenin А. А., Oks Е. М., Khasanov О. L., Dvilis E. S., Khasanov A. О. Electron beam sintering of ceramics. Journal – Electrotechnica & Electronica (Е+Е), Vol. 49 (5-6), 2014, pp. 315-318, ISSN: 0861-4717 (Print), 2603-5421 (Online)